Samyang Tribit® 1500G30 Polybutylene Terephthalate, 30% Glass Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1500G30 Polybutylene Terephthalate, 30% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics:G/F reinforcedHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm @Thickness 3.00 mm |
0.0020 - 0.012 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 50 g/10 min @Load 5.00 kg, Temperature 250 °C |
50 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 132 MPa | 19200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Flexural Modulus | 7.85 GPa | 1140 ksi | ASTM D790 |
| Izod Impact, Unnotched | 1.08 J/cm @Thickness 3.17 mm |
2.02 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 226 °C | 439 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Front Barrel Temperature | 220 - 230 °C | 428 - 446 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 265 °C | 509 °F | |
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | 0.010 - 0.015 % | 0.010 - 0.015 % | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-(14) 14 MFI Polycarbonate With Release
- Humiseal 1C55 Silicone Conformal Coating
- EMS-Griltech Grilon® M 371 White Nylon 6 Fiber
- DuPont™ Kapton® 200ZT Polyimide Film, 50 Micron Thickness
- Adamas Adalon® 826 PTFE, 50% Stainless steel
- 3M FM152 Indoor UL Recognized Computer Imprintable Silver Polyester Label Product
- BASF Neopolen® P 9255 0.09 g/cc Core density; Expanded Polypropylene (Europe)
- 3M Scotchcal™ 1000-58 Graphic Film
- 3M Tartan™ 305 General Purpose Box Sealing Tape
- Aclo Accutech Polypropylene Copolymer CP0436M20L Mica Reinforced
Copyright © lookpolymers.com All Rights Reserved