LATI Latiblend 6252 H2 G/30 PA6/PP Homopolymer

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Polypropylene (PP)
Manufacturer LATI
Trade Name Latiblend
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latiblend 6252 H2 G/30 PA6/PP Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Blend based on Polyamide 6 (PA6) / Polypropylene homopolymer (PPh). Heat stabilized. Glass fibers. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0050 cm/cm
0.0035 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 27.0 MPa
<br>@Temperature 150 °C
 3920 psi
<br>@Temperature 302 °F
40.0 MPa
<br>@Temperature 120 °C
 5800 psi
<br>@Temperature 248 °F
53.0 MPa
<br>@Temperature 90.0 °C
 7690 psi
<br>@Temperature 194 °F
78.0 MPa
<br>@Temperature 60.0 °C
 11300 psi
<br>@Temperature 140 °F
125 MPa
<br>@Temperature 23.0 °C
 18100 psi
<br>@Temperature 73.4 °F
Elongation at Break 2.7 %
<br>@Temperature 23.0 °C
 2.7 %
<br>@Temperature 73.4 °F
4.6 %
<br>@Temperature 60.0 °C
 4.6 %
<br>@Temperature 140 °F
6.0 %
<br>@Temperature 90.0 °C
 6.0 %
<br>@Temperature 194 °F
6.7 %
<br>@Temperature 120 °C
 6.7 %
<br>@Temperature 248 °F
7.5 %
<br>@Temperature 150 °C
 7.5 %
<br>@Temperature 302 °F
Elongation at Yield 4.0 %
<br>@Temperature 60.0 °C
 4.0 %
<br>@Temperature 140 °F
5.0 %
<br>@Temperature 90.0 °C
 5.0 %
<br>@Temperature 194 °F
6.0 %
<br>@Temperature 120 °C
 6.0 %
<br>@Temperature 248 °F
6.8 %
<br>@Temperature 150 °C
 6.8 %
<br>@Temperature 302 °F
Tensile Modulus 2.10 GPa
<br>@Temperature 150 °C
 305 ksi
<br>@Temperature 302 °F
3.10 GPa
<br>@Temperature 120 °C
 450 ksi
<br>@Temperature 248 °F
4.70 GPa
<br>@Temperature 90.0 °C
 682 ksi
<br>@Temperature 194 °F
6.40 GPa
<br>@Temperature 60.0 °C
 928 ksi
<br>@Temperature 140 °F
9.40 GPa
<br>@Temperature 23.0 °C
 1360 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²
<br>@Temperature 23.0 °C
 26.2 ft-lb/in²
<br>@Temperature 73.4 °F
5.50 J/cm²
<br>@Temperature -20.0 °C
 26.2 ft-lb/in²
<br>@Temperature -4.00 °F
Charpy Impact, Notched 0.800 J/cm²
<br>@Temperature -20.0 °C
 3.81 ft-lb/in²
<br>@Temperature -4.00 °F
1.00 J/cm²
<br>@Temperature 23.0 °C
 4.76 ft-lb/in²
<br>@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Vicat Softening Point 170 °C
<br>@Load 5.00 kg
 338 °F
<br>@Load 11.0 lb
Flammability, UL94 HB
<br>@Thickness 0.750 mm
 HB
<br>@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 70.0 - 80.0 °C
158 - 176 °F
Drying Temperature 80.0 - 90.0 °C
<br>@Time 10800 sec
 176 - 194 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa