LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Flame Retardant
Manufacturer LATI
Trade Name Later
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0095 - 0.0125 cm/cm
0.0095 - 0.0125 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa

@Temperature 150 °C
 5800 psi

@Temperature 302 °F
50.0 MPa

@Temperature 120 °C
 7250 psi

@Temperature 248 °F
65.0 MPa

@Temperature 90.0 °C
 9430 psi

@Temperature 194 °F
85.0 MPa

@Temperature 60.0 °C
 12300 psi

@Temperature 140 °F
120 MPa

@Temperature 23.0 °C
 17400 psi

@Temperature 73.4 °F
Elongation at Break 2.8 %

@Temperature 23.0 °C
 2.8 %

@Temperature 73.4 °F
4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
6.0 %

@Temperature 90.0 °C
 6.0 %

@Temperature 194 °F
6.2 %

@Temperature 120 °C
 6.2 %

@Temperature 248 °F
6.3 %

@Temperature 150 °C
 6.3 %

@Temperature 302 °F
Tensile Modulus 2.80 GPa

@Temperature 150 °C
 406 ksi

@Temperature 302 °F
3.80 GPa

@Temperature 120 °C
 551 ksi

@Temperature 248 °F
4.90 GPa

@Temperature 90.0 °C
 711 ksi

@Temperature 194 °F
7.20 GPa

@Temperature 60.0 °C
 1040 ksi

@Temperature 140 °F
9.50 GPa

@Temperature 23.0 °C
 1380 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
5.00 J/cm²

@Temperature -20.0 °C
 23.8 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.700 J/cm²

@Temperature -20.0 °C
 3.33 ft-lb/in²

@Temperature -4.00 °F
0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 31 %
31 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa