Materion Beryllium Copper Alloy 25 Strip; HT (TH04) Temper (UNS C17200)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 25 Strip; HT (TH04) Temper (UNS C17200).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: 2 hrs @ 315ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 98%Stress Relaxation after 1000 hrs @ 200°C: 74%Superficial Hardness: 30N 58-65Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 38 - 45 | 38 - 45 | |
| Hardness, Vickers | 373 - 446 | 373 - 446 | |
| Tensile Strength, Ultimate | 1310 - 1520 MPa | 190000 - 220000 psi | |
| Tensile Strength, Yield | 1130 - 1420 MPa | 164000 - 206000 psi | |
| Elongation at Break | 1.0 - 6.0 % | 1.0 - 6.0 % | |
| Modulus of Elasticity | 131 GPa | 19000 ksi | |
| Fatigue Strength | 310 - 340 MPa @# of Cycles 1.00e+8 |
45000 - 49300 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 105 W/m-K | 729 BTU-in/hr-ft²-°F | |
| Melting Point | 870 - 980 °C | 1600 - 1800 °F | |
| Solidus | 870 °C | 1600 °F | |
| Liquidus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 1.8 - 2.0 % | 1.8 - 2.0 % | |
| Co + Ni | >= 0.20 % | >= 0.20 % | |
| Co + Ni + Fe | <= 0.60 % | <= 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Lead, Pb | <= 0.020 % | <= 0.020 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000610 - 0.00000780 ohm-cm | 0.00000610 - 0.00000780 ohm-cm | 22-28% IACS Conductivity |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH T2020 Polypropylene Homopolymer, Mineral Reinforced
- Nilit FRIANYL A63 HS-GV40 Nylon 6.6 for injection molding, 40% glass fiber reinforced
- KYDEX® 6200 LTR Thermoforming Sheet for Mass Transit Applications
- Solvay Specialty Polymers Polidan® EC/MD Polyethylene, Crosslinked (XLPE)
- Spartech Litho SP-2090 Polystyrene Sheet
- Sharadaa Ceramics Resin Bonded Mattresses
- Teknor Apex APEX® 1700-70 Polyvinyl Chloride, Flexible
- A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
- Polyram RamSter PF702 PBT, UV Stabilized
- A. Schulman POLYBATCH™ Blue 4021 Concentrate Based in Polyethylene
Copyright © lookpolymers.com All Rights Reserved