LATI Latene® EP 7 TES/30 PP Copolymer, 30% Talc filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® EP 7 TES/30 PP Copolymer, 30% Talc filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene copolymer (PPc) based compound. Aesthetic talc. Very good surface appearance. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0095 - 0.0125 cm/cm | 0.0095 - 0.0125 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | |
| Elongation at Break | 35 % @Temperature 23.0 °C |
35 % @Temperature 73.4 °F |
|
| >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 5.0 % @Temperature 60.0 °C |
5.0 % @Temperature 140 °F |
||
| 6.0 % @Temperature 90.0 °C |
6.0 % @Temperature 194 °F |
||
| Tensile Modulus | 0.500 GPa @Temperature 90.0 °C |
72.5 ksi @Temperature 194 °F |
|
| 1.10 GPa @Temperature 60.0 °C |
160 ksi @Temperature 140 °F |
||
| 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
|
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
||
| Charpy Impact, Notched | 0.0300 J/cm² @Temperature -20.0 °C |
0.143 ft-lb/in² @Temperature -4.00 °F |
|
| 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 70.0 °C @Load 5.00 kg |
158 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- RheTech Products FT4900-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- NextGen Adhesives P907-12 Fiber Optic Adhesive
- A. Schulman POLYBATCH™ Ivory 90034/4 Concentrate Based In LDPE
- Chase Plastics CP Pryme® N120GL (COND, 50% RH) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated
- Borealis Nepol™ GB601HP Polypropylene, 30% Long Glass Fiber Reinforced w/HK060AE
- Dow Corning SYL-OFF® PMCPSL 6 Crosslinker
- Biomer P240 PHB Biodegradable Polymer
- BecauseWeCare BF90 Biodegradable Plastic
Copyright © lookpolymers.com All Rights Reserved