Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.021 g/cc | 0.03689 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.00 GPa | 145 ksi | ASTM D638 |
| Flexural Strength | 17.0 MPa | 2470 psi | ASTM D790 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
| Izod Impact, Notched | 6.19 J/cm | 11.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N339 Filler
- Indium Corp. Indalloy 143 Lead Solder Alloy
- LATI Latigray 37 B01-01 CX/35 Bio-Polymer
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- ExxonMobil Mobil Delvac Xtreme Service Grease
- Colorite Polymers 8200FR General Purpose Vinyl Compound
- Arkema Group OREVAC® 18760 Grafted Maleic Anhydride Polypropylene
- Goodfellow Titanium 80/Chromium 20 Alloy
- Lucite International Diakon® Frost 902 80 Acrylic Polymer
Copyright © lookpolymers.com All Rights Reserved