Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 30% Glass Fiber Filler |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA11,MHL,18-050,GF30Rigid grade with glass fiber (30%) filler for injection molding. Available colors: black and natural. Light and heat stabilized.Rigidity. High compressive strength. Low linear expansion coefficient. Low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability.UL classification: UL94 HB RTI(C) 65/65/65Example applications: Wind turbine, casing.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.8 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | 5 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.24 J/cm² | 39.2 ft-lb/in² | |
| 8.39 J/cm² @Temperature -30.0 °C |
39.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.06 J/cm² | 9.80 ft-lb/in² | |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
||
| Oxygen Index | 22 % | 22 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 7.00e+13 ohm-cm | 7.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | |
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2112 FR V0 Natural Polyamide + PP
- PolyOne Geon™ Vinyl Wire & Cable JLK51L Polyvinyl Chloride, Flexible (PVC, Flexible)
- RheTech Products T40P105-01 40% Talc Reinforced Polypropylene, Black
- LG Chemical LUPOY GP5056F PC/ABS+GF5%, Flame Retardance
- Karina 771-48/1-BY-IS Black PVC Compound
- MTI ThermoStran® PA66-30C Long Carbon Fiber Compound
- A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Eurostar Staramide RF004XXC PA6, 20% Glass Fiber Filled, Injection Molded
- Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
Copyright © lookpolymers.com All Rights Reserved