LATI Latene® 7H2W TR/40 PP Homopolymer, Mineral Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® 7H2W TR/40 PP Homopolymer, Mineral Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. Mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0085 - 0.0105 cm/cm | 0.0085 - 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 13.0 MPa @Temperature 60.0 °C |
1890 psi @Temperature 140 °F |
|
| 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 35 % @Temperature 60.0 °C |
35 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
|
| 3.4 % @Temperature 60.0 °C |
3.4 % @Temperature 140 °F |
||
| 4.6 % @Temperature 90.0 °C |
4.6 % @Temperature 194 °F |
||
| Tensile Modulus | 1.00 GPa @Temperature 90.0 °C |
145 ksi @Temperature 194 °F |
|
| 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
||
| 4.90 GPa @Temperature 60.0 °C |
711 ksi @Temperature 140 °F |
||
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| Vicat Softening Point | 100 °C @Load 5.00 kg |
212 °F @Load 11.0 lb |
|
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Poco Graphite AXF-5QC Specialty Graphite, Copper Impregnated
- Nitriflex SB-1009 G Styrene Butadiene Copolymer
- Michelman® Hydrosize® HP-1632 Polyimide solution
- ChevronTexaco 128 Refined Wax
- DSM Akulon® K224-HG3 Nylon 6-15% Glass Reinforced (European and Asian Grade) (Cond)
- DuPont Performance Polymers Rynite® 530 BK503 Polyethylene Terephthalate (PET) (Unverified Data**)
- Epoxy Technology EPO-TEK® H20E-MP Electrically Conductive, Silver Epoxy
- BNZ Materials Blazecrete 3000 Dense Castable
- LATI Latimass 62-05 D040 PA6
Copyright © lookpolymers.com All Rights Reserved