Plaskolite Optix® CP - 927 High Impact Grade Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CP - 927 High Impact Grade Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 50.3 MPa | 7300 psi | ASTM D-638 |
| Elongation at Break | 5.3 % | 5.3 % | ASTM D-638 |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | ASTM D-638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D-790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm |
0.900 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 3.05 J @Thickness 3.17 mm |
2.25 ft-lb @Thickness 0.125 in |
Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D-696 |
| Maximum Service Temperature, Air | 50.0 °C | 122 °F | UL-746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.9 °C | 174 °F | ASTM D-648 |
| Vicat Softening Point | 112 °C | 233 °F | ASTM D-1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.8 % | <= 1.8 % | ASTM D-1003 |
| Transmission, Visible | 91.3 % | 91.3 % | ASTM D-1003 |
Users viewing this material also viewed the following:
- ITW Plexus Plexusâ„¢ MA300 Methacrylate Adhesive
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- Zoltek Pyron® Oxidized Felt
- ConocoPhillips ANDEROL® PQ AA 85W140 White Mineral Food Grade Gear Oil, ISO Grade 320, SAE Gear Oil Grade 85W140
- Asahi Glass Fluon® PB2510 10% Carbon Fiber, PTFE Filled Compound
- Sinotek Materials A Graphite Roll
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Zinc Stearate
Copyright © lookpolymers.com All Rights Reserved