LATI Latene® 7 TR-V2 PP Homopolymer, Mineral Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer LATI
Trade Name Latene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® 7 TR-V2 PP Homopolymer, Mineral Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene homopolymer (PPh) based compound. Mineral filler. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free. Good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
Linear Mold Shrinkage, Flow 0.0135 - 0.0165 cm/cm
0.0135 - 0.0165 in/in
Linear Mold Shrinkage, Transverse 0.014 - 0.017 cm/cm
0.014 - 0.017 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
3630 psi
Elongation at Break 25 %

@Temperature 23.0 °C
 25 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
Elongation at Yield 6.0 %

@Temperature 23.0 °C
 6.0 %

@Temperature 73.4 °F
8.0 %

@Temperature 60.0 °C
 8.0 %

@Temperature 140 °F
9.0 %

@Temperature 90.0 °C
 9.0 %

@Temperature 194 °F
Tensile Modulus 0.550 GPa

@Temperature 90.0 °C
 79.8 ksi

@Temperature 194 °F
0.950 GPa

@Temperature 60.0 °C
 138 ksi

@Temperature 140 °F
2.20 GPa

@Temperature 23.0 °C
 319 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -20.0 °C
 7.14 ft-lb/in²

@Temperature -4.00 °F
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.0300 J/cm²

@Temperature -20.0 °C
 0.143 ft-lb/in²

@Temperature -4.00 °F
0.150 J/cm²

@Temperature 23.0 °C
 0.714 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Vicat Softening Point 100 °C

@Load 5.00 kg
 212 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 29 %
29 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 220 °C
356 - 428 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa