LATI Latan 13 K/30 POM, 30% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | LATI |
| Trade Name | Latan |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latan 13 K/30 POM, 30% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyoxymethylene (POM) based compound. Carbon fiber. Medium viscosity. Good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0055 cm/cm | 0.0030 - 0.0055 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa @Temperature 90.0 °C |
9430 psi @Temperature 194 °F |
|
| 100 MPa @Temperature 60.0 °C |
14500 psi @Temperature 140 °F |
||
| 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
||
| Elongation at Break | 0.90 % @Temperature 23.0 °C |
0.90 % @Temperature 73.4 °F |
|
| 1.1 % @Temperature 60.0 °C |
1.1 % @Temperature 140 °F |
||
| 1.2 % @Temperature 90.0 °C |
1.2 % @Temperature 194 °F |
||
| Tensile Modulus | 10.0 GPa @Temperature 90.0 °C |
1450 ksi @Temperature 194 °F |
|
| 14.5 GPa @Temperature 60.0 °C |
2100 ksi @Temperature 140 °F |
||
| 18.5 GPa @Temperature 23.0 °C |
2680 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
|
| 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
||
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
|
| 0.250 J/cm² @Temperature 23.0 °C |
1.19 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
| Vicat Softening Point | 165 °C @Load 5.00 kg |
329 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- MV Labs LU800 Lu2O3 Lutetium oxide
- Quadrant EPP Ketron® GF30 PEEK, Extruded 30% Glass-Reinforced Polyetherether Ketone (ASTM Product Data Sheet)
- MetalTek MTEK 35-15 Cast UNS N08605 Heat Resistant Stainless Steel
- Seals Eastern 7042 Fluorocarbon-Elastomer
- Teknor Apex TEKRON® 4000-60 Thermoplastic Elastomer
- Teknor Apex Vidux® CV-1000-76 Polyvinyl Chloride, Flexible
- Ecomass® 4703ZD88 Tungsten Filled Polyurethane
- Eurotec® Tecotek® PC43 GR30 BK002 PC, 30% glass fiber reinforced, black
- Arkema Group LOTADER® 4603 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- China Tungsten YWC Tungsten Carbide for Dies and Wear Part Making
Copyright © lookpolymers.com All Rights Reserved