LATI Latamid SP2 H2 G/45 PA 6.12, 45% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid SP2 H2 G/45 PA 6.12, 45% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6.12 (PA6.12) based compound. Heat stabilized. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa

@Temperature 150 °C
 11600 psi

@Temperature 302 °F
100 MPa

@Temperature 120 °C
 14500 psi

@Temperature 248 °F
115 MPa

@Temperature 90.0 °C
 16700 psi

@Temperature 194 °F
140 MPa

@Temperature 60.0 °C
 20300 psi

@Temperature 140 °F
190 MPa

@Temperature 23.0 °C
 27600 psi

@Temperature 73.4 °F
Elongation at Break 3.3 %

@Temperature 23.0 °C
 3.3 %

@Temperature 73.4 °F
4.3 %

@Temperature 60.0 °C
 4.3 %

@Temperature 140 °F
5.0 %

@Temperature 90.0 °C
 5.0 %

@Temperature 194 °F
5.5 %

@Temperature 120 °C
 5.5 %

@Temperature 248 °F
6.2 %

@Temperature 150 °C
 6.2 %

@Temperature 302 °F
Tensile Modulus 4.00 GPa

@Temperature 150 °C
 580 ksi

@Temperature 302 °F
4.80 GPa

@Temperature 120 °C
 696 ksi

@Temperature 248 °F
6.90 GPa

@Temperature 90.0 °C
 1000 ksi

@Temperature 194 °F
8.00 GPa

@Temperature 60.0 °C
 1160 ksi

@Temperature 140 °F
11.5 GPa

@Temperature 23.0 °C
 1670 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 210 °C

@Load 5.00 kg
 410 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 - 100 °C

@Time 10800 sec
 176 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa