- ITW Devcon Metal Repair Aluminum Putty (F), Aluminum
ITW Devcon Metal Repair Aluminum Putty (F), Aluminum
| Category | Polymer , Adhesive , Thermoset |
| Manufacturer | ITW Devcon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ITW Devcon Metal Repair Aluminum Putty (F), Aluminum.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by ITW Devcon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | Cured; ASTM D2240 |
| Tensile Strength at Break | 25.4 MPa | 3680 psi | ASTM D638 |
| Modulus of Elasticity | 5.52 GPa | 800 ksi | ASTM D638 |
| Flexural Strength | 46.6 MPa | 6760 psi | ASTM D790 |
| Compressive Strength | 58.1 MPa | 8420 psi | ASTM D695 |
| Adhesive Bond Strength | 17.9 MPa | 2600 psi | tensile shear; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 52.2 µm/m-°C @Temperature 20.0 °C |
29.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.724 W/m-K | 5.02 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 121 °C | 250 °F | dry |
| Shrinkage | 0.080 % | 0.080 % | Cured; ASTM D2566 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 21.4 @Frequency 1000 Hz |
21.4 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 3.94 kV/mm | 100 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 960 min | 16.0 hour | Functional cure |
| Pot Life | 60.0 min @Temperature 23.9 °C |
60.0 min @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage per pound, in² @ 1/4" thickness | 70 | |
| Mix ratio by volume (Resin:Hardener) | 4:1 | |
| Mix ratio by weight (Resin:Hardener) | 9:1 |
Users viewing this material also viewed the following:
- Samyang Triloy® 410N PC/PET alloy, Flame Retardant (discontinued **)
- Polimeri Europa Extir® P 1212 Expandable Polystyrene (discontinued **)
- PolyOne Geon™ Vinyl Flexible R3792C Polyvinyl Chloride, Flexible (PVC, Flexible)
- Hexion Bakelite™ PF 2535 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof (discontinued **
- Lotte Chemical Titan TITANPRO® SM461 Polypropylene random copolymer
- A. Schulman FORMION™ FI 395 Ionomer
- A. Schulman POLYBATCH™ PT10327 Amber Concentrate Based in PET
- Zylog Neoplast® 135 FT EB Thermoplastic Vulcanizate
- Enviro Tech International EnSolv® n-Propyl Bromide Vapor Degreasing Solvent
- Abatron 8506-2A/503B Filled Potting Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved