Victrex® PEEK 90HMF20 Polyetheretherketone (PEEK), 20% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 90HMF20 Polyetheretherketone (PEEK), 20% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: High performance thermoplastic material, 20% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, very easy flow, color black.Typical Application Areas: Complex geometries with thinner cross sections or longer flow length where superior strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.All information provided by Victrex.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc

@Temperature 23.0 °C
 1.37 g/cc

@Temperature 73.4 °F
 Crystalline; ISO 1183
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 immersion; ISO 62-1
0.50 %

@Temperature 100 °C
 0.50 %

@Temperature 212 °F
 immersion; ISO 62-1
Viscosity 175000 cP

@Temperature 400 °C
 175000 cP

@Temperature 752 °F
 Melt; ISO 11443
Linear Mold Shrinkage, Flow 0.00 cm/cm
0.00 in/in
85°C nozzle, 190°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
85°C nozzle, 190°C tool; ISO 294-4
Spiral Flow 18.0 cm

@Thickness 1.00 mm
 7.09 in

@Thickness 0.0394 in
 85°C nozzle, 190°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 86.5
86.5
ISO 868
Tensile Strength at Break 80.0 MPa

@Temperature 275 °C
 11600 psi

@Temperature 527 °F
 ISO 527
120 MPa

@Temperature 175 °C
 17400 psi

@Temperature 347 °F
 ISO 527
190 MPa

@Temperature 125 °C
 27600 psi

@Temperature 257 °F
 ISO 527
290 MPa

@Temperature 23.0 °C
 42100 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Yield 1.9 %

@Temperature 23.0 °C
 1.9 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 22.0 GPa

@Temperature 23.0 °C
 3190 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 100 MPa

@Temperature 275 °C
 14500 psi

@Temperature 527 °F
 ISO 178
180 MPa

@Temperature 175 °C
 26100 psi

@Temperature 347 °F
 ISO 178
290 MPa

@Temperature 125 °C
 42100 psi

@Temperature 257 °F
 ISO 178
400 MPa

@Temperature 23.0 °C
 58000 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 20.0 GPa

@Temperature 23.0 °C
 2900 ksi

@Temperature 73.4 °F
 ISO 178
Compressive Strength 90.0 MPa

@Temperature 200 °C
 13100 psi

@Temperature 392 °F
 ISO 604
200 MPa

@Temperature 120 °C
 29000 psi

@Temperature 248 °F
 ISO 604
270 MPa

@Temperature 23.0 °C
 39200 psi

@Temperature 73.4 °F
 ISO 604
Izod Impact, Notched (ISO) 8.50 kJ/m²

@Temperature 23.0 °C
 4.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Izod Impact, Unnotched (ISO) 60.0 kJ/m²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Charpy Impact Unnotched 6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1U
Charpy Impact, Notched 0.750 J/cm²

@Temperature 23.0 °C
 3.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature <=143 °C
 22.2 µin/in-°F

@Temperature <=289 °F
 Average below Tg; ISO 11359
100 µm/m-°C

@Temperature >=143 °C
 55.6 µin/in-°F

@Temperature >=289 °F
 Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 3.00 µm/m-°C

@Temperature >=143 °C
 1.67 µin/in-°F

@Temperature >=289 °F
 Above Tg; ISO 11359
5.50 µm/m-°C

@Temperature <=143 °C
 3.06 µin/in-°F

@Temperature <=289 °F
 Below Tg; ISO 11359
Thermal Conductivity 1.00 W/m-K

@Temperature 23.0 °C
 6.94 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
 Average; ISO 22007-4
1.90 W/m-K

@Temperature 23.0 °C
 13.2 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
 Along flow; ISO 22007-4
Melting Point 343 °C
649 °F
Onset; ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 347 °C
657 °F
ISO 75A-f
Glass Transition Temp, Tg 143 °C
289 °F
ISO 11357
Electrical Properties Metric English Comments
Volume Resistivity 1e+05
1e+05
1V; ASTM D4496
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 385 °C
725 °F
Mold Temperature 180 - 200 °C
356 - 392 °F
Drying Temperature 120 °C

@Time 7200 sec
 248 °F

@Time 2.00 hour
150 °C

@Time 10800 sec
 302 °F

@Time 3.00 hour