LATI Latamid SP1 G/30 PA 6.10, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid SP1 G/30 PA 6.10, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6.10 (PA6.10) based compound. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0065 cm/cm
0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
85.0 MPa

@Temperature 120 °C
 12300 psi

@Temperature 248 °F
100 MPa

@Temperature 90.0 °C
 14500 psi

@Temperature 194 °F
120 MPa

@Temperature 60.0 °C
 17400 psi

@Temperature 140 °F
165 MPa

@Temperature 23.0 °C
 23900 psi

@Temperature 73.4 °F
Elongation at Break 3.2 %

@Temperature 23.0 °C
 3.2 %

@Temperature 73.4 °F
4.2 %

@Temperature 60.0 °C
 4.2 %

@Temperature 140 °F
4.9 %

@Temperature 90.0 °C
 4.9 %

@Temperature 194 °F
5.4 %

@Temperature 120 °C
 5.4 %

@Temperature 248 °F
6.1 %

@Temperature 150 °C
 6.1 %

@Temperature 302 °F
Tensile Modulus 3.00 GPa

@Temperature 150 °C
 435 ksi

@Temperature 302 °F
3.60 GPa

@Temperature 120 °C
 522 ksi

@Temperature 248 °F
5.30 GPa

@Temperature 90.0 °C
 769 ksi

@Temperature 194 °F
6.20 GPa

@Temperature 60.0 °C
 899 ksi

@Temperature 140 °F
8.80 GPa

@Temperature 23.0 °C
 1280 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 10.0 J/cm²
47.6 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
 428 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 70.0 - 90.0 °C

@Time 10800 sec
 158 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa