- PolyOne Edgetek® PI-40CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **)
PolyOne Edgetek® PI-40CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PI-40CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Thickness 3.17 mm |
0.10 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 255 MPa | 37000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 19.3 GPa | 2800 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 331 MPa | 48000 psi | ASTM D790 |
| Flexural Modulus | 19.3 GPa | 2800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.30 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 388 - 421 °C | 730 - 790 °F | Molding |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckfip™ FIP-E Formed in Place Conductive Elastomer
- Momentive Performance Materials TUFELâ„¢ II 94305 Low Volatile Extrusion Heat Cured Rubber
- Samyang Tripet® 2550GN30 Polyethylene Terephthalate, 30% Glass Fiber Reinforced, Flame Retardant
- ExxonMobil 50 Mobiltrans HD
- ExxonMobil Exxtral™ HMU 210 Performance Polyolefin
- 3M 31825 Industrial Polyethylene Temporary Surface Protection Tape
- Aclo Accutech Polypropylene Homopolymer HP0334G10CL Glass Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved