SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX 553 is a 30% glass fibre reinforced, flame retardant PBT+PC blend with good warpage characteristics. Applications: appliance handles, spotlights, electric motors, pumphousings.
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D792
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Filler Content 30 %
30 %
ASTM D229
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.26 %
0.26 %
ISO 62
Viscosity 200000 cP
200000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on Tensile Bar; SABIC Method
0.0050 cm/cm

@Thickness 3.20 mm
 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0090 cm/cm
0.0050 - 0.0090 in/in
on Tensile Bar; SABIC Method
Melt Flow 40 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 40 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
20 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
30 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 30 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ISO 2039-2
Hardness, H358/30 132 MPa
19100 psi
ISO 2039-1
Tensile Strength at Break 135 MPa
19600 psi
5 mm/min; ISO 527
140 MPa
20300 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 135 MPa
19600 psi
5 mm/min; ISO 527
140 MPa
20300 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Flexural Strain, break, 2 mm/min; ISO 178
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 10.7 GPa
1550 ksi
5 mm/min; ASTM D638
11.0 GPa
1600 ksi
1 mm/min; ISO 527
Flexural Strength 190 MPa
27600 psi
1.3 mm/min, 50 mm span; ASTM D790
200 MPa
29000 psi
2 mm/min; ISO 178
Flexural Yield Strength 190 MPa
27600 psi
1.3 mm/min, 50 mm span; ASTM D790
205 MPa
29700 psi
2 mm/min; ISO 178
Flexural Modulus 9.40 GPa
1360 ksi
1.3 mm/min, 50 mm span; ASTM D790
9.50 GPa
1380 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
ASTM D256
0.900 J/cm

@Temperature -30.0 °C
 1.69 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
0.950 J/cm

@Temperature 0.000 °C
 1.78 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
Izod Impact, Unnotched 7.70 J/cm
14.4 ft-lb/in
ASTM D4812
7.70 J/cm

@Temperature -30.0 °C
 14.4 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
45.0 kJ/m²
21.4 ft-lb/in²
Izod Reverse Impact, notched 80*10*4,23°C; ISO 180/1C
9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature 0.000 °C
 4.76 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²
25.2 ft-lb/in²
80*10*4; ISO 180/1U
52.0 kJ/m²

@Temperature -30.0 °C
 24.7 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/2C
NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.10 J/cm²
5.23 ft-lb/in²
ISO 179/2C
0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
 3.3

@Frequency 1.00e+6 Hz
 IEC 60250
3.4

@Frequency 50.0 - 60.0 Hz
 3.4

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 15.0 kV/mm

@Thickness 3.20 mm
 381 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
15.0 kV/mm

@Thickness 3.20 mm
 381 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
28.0 kV/mm

@Thickness 0.800 mm
 711 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
28.0 kV/mm

@Thickness 0.800 mm
 711 kV/in

@Thickness 0.0315 in
 in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0070

@Frequency 1.00e+6 Hz
 0.0070

@Frequency 1.00e+6 Hz
 IEC 60250
0.020

@Frequency 2.45e+9 Hz
 0.020

@Frequency 2.45e+9 Hz
 IEC 60250
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index >= 125 V
>= 125 V
IEC 60112
175 - 250 V
175 - 250 V
UL 746A
225 V
225 V
IEC 60112