- Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled
- LATI Lastilac RT K/10 ABS, 10% Carbon Fiber Reinforced
LATI Lastilac RT K/10 ABS, 10% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Lastilac |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Lastilac RT K/10 ABS, 10% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Carbon fiber. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0040 cm/cm | 0.0025 - 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa @Temperature 90.0 °C |
4350 psi @Temperature 194 °F |
|
| 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
||
| 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
||
| Elongation at Break | 0.70 % @Temperature 23.0 °C |
0.70 % @Temperature 73.4 °F |
|
| 0.70 % @Temperature 60.0 °C |
0.70 % @Temperature 140 °F |
||
| 0.70 % @Temperature 90.0 °C |
0.70 % @Temperature 194 °F |
||
| Elongation at Yield | 0.60 % @Temperature 90.0 °C |
0.60 % @Temperature 194 °F |
|
| Tensile Modulus | 6.00 GPa @Temperature 90.0 °C |
870 ksi @Temperature 194 °F |
|
| 7.50 GPa @Temperature 60.0 °C |
1090 ksi @Temperature 140 °F |
||
| 8.30 GPa @Temperature 23.0 °C |
1200 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
|
| 1.00 J/cm² @Temperature -20.0 °C |
4.76 ft-lb/in² @Temperature -4.00 °F |
||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
|
| 0.450 J/cm² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
| Vicat Softening Point | 105 °C @Load 5.00 kg |
221 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2000 ohm | 2000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 70.0 - 80.0 °C @Time 10800 sec |
158 - 176 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufGuard E™ XP-115DD-Zeta PE, Flame Retardant
- ExxonMobil LL 3301.63 Premium High Strength Film Resin (discontinued **)
- SABIC Innovative Plastics Lexan® 3412R PC (Europe-Africa-Middle East)
- Taiwan PU Corporation TPU-EH80 High Hydrolysis Resistance, Extrusion Molding Polyether Base TPU
- SABIC Innovative Plastics Ultem 1010V PEI (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT (Asia Pacific)
- A. Schulman POLYBATCH™ Light Blue 40442 Concentrate Based In LLDPE
- Axiall 8941 Moldings & Extrusions Flexible PVC
- BASF 3-Dimethylaminopropane-1-ol
Copyright © lookpolymers.com All Rights Reserved