Shell Carilon® D26HM100 Polyketone, General-Purpose Injection Molding Grade  (discontinued **)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® D26HM100 Polyketone, General-Purpose Injection Molding Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26HM100 is a general-purpose injection molding grade with mechanical properties which classify it as an engineering thermoplastic. This grade has an excellent balance of stiffness and toughness over a broad temperature range, high resilience and good wear resistance. CARILON Polymer D26HM100 can also withstand short-term exposure to elevated temperatures. Moreover this polymer exhibits a high resistance to hydrocarbons, solvents, salt solutions, weak acids and weak bases.CARILON Polymer D26HM100 is easy to process on standard injection molding equipment. Cycle times are generally short. Parts show good mold definition with glossy mar-resistant surfaces. CARILON Polymers' low moisture sensitivity means that no conditioning of parts before assembly or use is necessary.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption 0.45 %
0.45 %
24 hour immersion; ASTM D570
Moisture Absorption at Equilibrium 0.50 %
0.50 %
at 50% RH at Equilibrium; ASTM D570
Water Absorption at Saturation 2.1 %
2.1 %
at saturation; ASTM D570
Linear Mold Shrinkage, Flow 0.022 cm/cm
0.022 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 240 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 464 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Hardness, Shore D 75
75
ISO 868
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM D638
Elongation at Break >= 300 %
>= 300 %
ASTM D638
Elongation at Yield 22 %
22 %
ASTM D638
Tensile Modulus 1.60 GPa
232 ksi
ASTM D638
Flexural Strength 55.0 MPa
7980 psi
at 5% strain; ASTM D790
Flexural Modulus 1.60 GPa
232 ksi
ASTM D790
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
0.500 J/cm

@Temperature -40.0 °C
0.937 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
ISO 179
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Gardner Impact >= 45.0 J
>= 33.2 ft-lb
28.0 J

@Temperature -40.0 °C
20.7 ft-lb

@Temperature -40.0 °F
Tensile Impact Strength 210 kJ/m²
99.9 ft-lb/in²
ASTM D1822
Coefficient of Friction, Dynamic 0.49
0.49
Thrust washer testing against steel at 0.05 m/s (2 in/s) and 2 MPa
Limiting Pressure Velocity 1.10 MPa-m/sec
31400 psi-ft/min
Thrust Washer at 0.5 m/s
Taber Abrasion, mg/1000 Cycles 12
12
1 kg load; CS-17 Wheel; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 110 µm/m-°C

@Temperature 25.0 - 55.0 °C
61.1 µin/in-°F

@Temperature 77.0 - 131 °F
ASTM E831
Melting Point 220 °C
428 °F
Maximum Service Temperature, Air 90.0 °C
194 °F
UL-746B Long Term Relative temperature Index; Mechanical w/o Impact
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ASTM D648
Vicat Softening Point 210 °C
410 °F
ASTM D1525
UL RTI, Mechanical with Impact 85.0 °C

@Thickness 0.750 mm
185 °F

@Thickness 0.0295 in
UL-746B
UL RTI, Mechanical without Impact 90.0 °C

@Thickness 0.750 mm
194 °F

@Thickness 0.0295 in
UL-746B
Flammability, UL94 HB
HB
Oxygen Index 21 %
21 %
ISO 4589
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Dielectric Constant 5.7

@Frequency 1e+6 Hz
5.7

@Frequency 1e+6 Hz
ASTM D150
6.3

@Frequency 1000 Hz
6.3

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 1.60 mm
533 kV/in

@Thickness 0.0630 in
Short Term; ASTM D149
Dissipation Factor 0.010

@Frequency 1000 Hz
0.010

@Frequency 1000 Hz
ASTM D150
0.060

@Frequency 1e+6 Hz
0.060

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 100 sec
100 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
UL746A