LATI Laril 13 G/10-V1 PPOm, 10% Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled
Manufacturer LATI
Trade Name Laril
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laril 13 G/10-V1 PPOm, 10% Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. UL94 V-1 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Very high dimensional stability. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
Linear Mold Shrinkage, Flow 0.0045 - 0.0070 cm/cm
0.0045 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa

@Temperature 120 °C
 2180 psi

@Temperature 248 °F
35.0 MPa

@Temperature 90.0 °C
 5080 psi

@Temperature 194 °F
60.0 MPa

@Temperature 60.0 °C
 8700 psi

@Temperature 140 °F
65.0 MPa

@Temperature 23.0 °C
 9430 psi

@Temperature 73.4 °F
Elongation at Break 3.5 %

@Temperature 23.0 °C
 3.5 %

@Temperature 73.4 °F
3.5 %

@Temperature 60.0 °C
 3.5 %

@Temperature 140 °F
3.8 %

@Temperature 90.0 °C
 3.8 %

@Temperature 194 °F
4.5 %

@Temperature 120 °C
 4.5 %

@Temperature 248 °F
Elongation at Yield 2.0 %

@Temperature 90.0 °C
 2.0 %

@Temperature 194 °F
2.0 %

@Temperature 120 °C
 2.0 %

@Temperature 248 °F
Tensile Modulus 2.40 GPa

@Temperature 120 °C
 348 ksi

@Temperature 248 °F
2.80 GPa

@Temperature 90.0 °C
 406 ksi

@Temperature 194 °F
3.40 GPa

@Temperature 60.0 °C
 493 ksi

@Temperature 140 °F
4.00 GPa

@Temperature 23.0 °C
 580 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Vicat Softening Point 130 °C

@Load 5.00 kg
 266 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
Oxygen Index 28 %
28 %
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
A solution
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa