LATI Lapex R G/10 PPSU, 10% Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer LATI
Trade Name Lapex
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Lapex R G/10 PPSU, 10% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyphenylene Sulfone (PPSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
Linear Mold Shrinkage, Flow 0.0045 - 0.0060 cm/cm
0.0045 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0085 - 0.010 cm/cm
0.0085 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
<br>@Temperature 150 °C
 10200 psi
<br>@Temperature 302 °F
80.0 MPa
<br>@Temperature 120 °C
 11600 psi
<br>@Temperature 248 °F
90.0 MPa
<br>@Temperature 90.0 °C
 13100 psi
<br>@Temperature 194 °F
100 MPa
<br>@Temperature 60.0 °C
 14500 psi
<br>@Temperature 140 °F
105 MPa
<br>@Temperature 23.0 °C
 15200 psi
<br>@Temperature 73.4 °F
Elongation at Break 2.3 %
<br>@Temperature 150 °C
 2.3 %
<br>@Temperature 302 °F
2.5 %
<br>@Temperature 120 °C
 2.5 %
<br>@Temperature 248 °F
2.6 %
<br>@Temperature 60.0 °C
 2.6 %
<br>@Temperature 140 °F
2.6 %
<br>@Temperature 90.0 °C
 2.6 %
<br>@Temperature 194 °F
2.8 %
<br>@Temperature 23.0 °C
 2.8 %
<br>@Temperature 73.4 °F
Tensile Modulus 3.40 GPa
<br>@Temperature 150 °C
 493 ksi
<br>@Temperature 302 °F
3.55 GPa
<br>@Temperature 120 °C
 515 ksi
<br>@Temperature 248 °F
3.70 GPa
<br>@Temperature 90.0 °C
 537 ksi
<br>@Temperature 194 °F
3.85 GPa
<br>@Temperature 60.0 °C
 558 ksi
<br>@Temperature 140 °F
4.00 GPa
<br>@Temperature 23.0 °C
 580 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 190 °C
374 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Vicat Softening Point 220 °C
<br>@Load 5.00 kg
 428 °F
<br>@Load 11.0 lb
Flammability, UL94 V-0
<br>@Thickness 3.00 mm
 V-0
<br>@Thickness 0.118 in
V-0
<br>@Thickness 1.50 mm
 V-0
<br>@Thickness 0.0591 in
Oxygen Index 38 %
38 %
Processing Properties Metric English Comments
Melt Temperature 350 - 390 °C
662 - 734 °F
Mold Temperature 150 - 190 °C
302 - 374 °F
Drying Temperature 140 - 180 °C
<br>@Time 10800 sec
 284 - 356 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa