Kolon KOPA® KN333HI5BL High Impact Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333HI5BL High Impact Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Middle viscosity, Impact -resistantApplications A variety of fuse boxes, relax boxesInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.256 GPa | 327.2 ksi | ASTM D790 |
| Izod Impact, Notched | 4.90 J/cm | 9.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 | 3.1 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 6208 BLK
- MV Labs IN400 InCl3 Indium(III) chloride
- Precision Polymer Engineering S60T Silicone Rubber
- Isoflon Tisoflon® 5G Polytetrafluoroethylene & Graphite Coated Glass Fabric
- LATI Latamid 66 H2 G/50-V0KB1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Saint-Gobain CHR® SG23-06(R) Primary Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- ChevronTexaco ISO 150 Red Chain Bar Oil
- Addcomp ADD-VANCE® FR 495 PP copolymer based flame-retardant compound
- 3M 3325 Copper Foil Tape
- Fainplast Compounds PM 6010 Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved