Kolon KOPA® KN1322VO Flame Retardant Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN1322VO Flame Retardant Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 83.4 MPa | 12100 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 40 % | 40 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 3.04 GPa | 441 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm | 1.29 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 220 °C | 428 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 115 sec | 115 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Anti-Seize Aluminum Paste
- Materion Beryllium Copper Alloy M25 Rod and Bar; AT (TF00) Temper; over 76 mm (UNS C17300)
- KKPC KOSYN KSL 101 Styrene-Butadiene Latex
- Techmer ES HiFill® PA6/6 GF25 HS L BK 25% Glass Filled
- ExxonMobil Escorene™ UL 40028CC Ethylene Vinyl Acetate Copolymer (European Grade)
- Eurostar Staramide AG6ST43H PA66, Glass Fiber Reinforced, Impact Modified, Injection Molding
- Adell YS-10 PC Alloy
- Ascend Performance Materials Vydyne® 21SPG1 Nylon 66, Conditioned
- Aaron Industries AAROPRENE® MFN 6601 Mineral Filled Nylon 6/6
- Loctite® Durabond® E-00CL Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved