Kingfa CPA-6 Toughened PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa CPA-6 Toughened PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:High impactLow tendency to wrapApplications:Injection moldingSport applianceAutomobile partsPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc @Temperature 23.0 °C |
1.08 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm @Temperature 23.0 °C |
0.014 - 0.018 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 10mm/min; ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | 10mm/min; ASTM D638 |
| Flexural Strength | 63.0 MPa | 9140 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 1.68 GPa | 244 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 7.80 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
14.6 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C @Thickness 6.40 mm |
406 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C @Thickness 6.40 mm |
136 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 300 °C | <= 572 °F | |
| Rear Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Start Point: 230°C |
| Middle Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Start Point: 255°C |
| Front Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Start Point: 265°C |
| Melt Temperature | 255 - 285 °C | 491 - 545 °F | Start Point: 265°C |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Start Point: 60°C |
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate to High |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 1200 A 43 HS Natural Polyamide 66 (Nylon 66)
- Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK) (Unverified Data**)
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet
- Shakespeare NX-806 Saltwater Nylon Copolymer Fishing Line, 14 lb
- SABIC Innovative Plastics LNP VERTON UV00AS PPA (Asia Pacific)
- Vesta Ceramics SicoMill® Grade 2 Silicon Powder
- Westlake MC2004 High Density Polyethylene Coating
- DuPont Teijin Films Melinex® 329 Polyester Film, 700 Gauge
- Adamas Adalon® 237 PTFE, 25% Glass Fiber
- Fainplast Compounds FKA 88/1 Flexible PVC, Flame Retardant Insulation Lead Free
Copyright © lookpolymers.com All Rights Reserved