Inno-Comp INNOPOL® CS 1-3000 B DEL Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-3000 B DEL Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-3000 B DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc @Temperature 23.0 °C |
0.0332 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0117 cm/cm | 0.0117 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0096 cm/cm | 0.0096 in/in | ISO 294 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 14 % | 14 % | ISO 527-1,-2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.65 GPa | 239 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.120 J/cm² @Temperature -30.0 °C |
0.571 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.370 J/cm² @Temperature 23.0 °C |
1.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 162 °C | 324 °F | DSC; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1,-2 |
| Vicat Softening Point | 94.0 °C | 201 °F | B120; ISO 306 |
| 153 °C | 307 °F | A120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive Materials | Pass | FMVSS 302 |
| Color | Black |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC
- Lucent Polymers PC-1403 Polycarbonate, Extrusion/Blow Molding Grade
- Techmer ES HiFill® PA6 0137 S2
- Supreme Petrochem SP 256 Toughened Polystyrene
- Hexcel® HexWeb® CR III 3/8-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Cossa Polimeri ESTABLEND PSA 8500 V0 Flame Retardant PC / ASA Blend
- ExxonMobil LDPE LD 506.07 Low Density Polyethylene Resin
- Aclo Accutech Polypropylene Homopolymer HP0334M10CL Mica Reinforced Coupled
- Aremco Corr-Paint™ CP4010-S1 High Temperature Protective Coating, Silicone
Copyright © lookpolymers.com All Rights Reserved