Ineos Nova Zyntar® 7041 High Performance Flame Retardant Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos Nova Zyntar® 7041 High Performance Flame Retardant Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-Decabromodiphenyl Oxide, High flow, Ease of processingApplications: Electronics, TelevisionsThis is an impact grade of polystyrene containing chemicals to increase resistance to ignition in laboratory flame tests. Laboratory flame tests are not intended to appraise the hazards of material under actual fire conditions. It has be processed at normal condition on a variety of machines. melt temperatures about 470°F should be avoided to prevent degradation and possible machine damage through corrosion and/or high internal pressure. Therefore, processing equipment should be flushed out with polystyrene that does not contain flame retardants whenever an appreciable interruption of cycle occurs. Organic polymers containing flame retardant additives may release hazardous or toxic vapors if given lengthy or excessive exposure to high heat. Adequate ventilation should be used during processing.Injection Speed: Slow to ModerateColored material may differ in some properties. All molded samples were an 1/8 inch thick unless noted.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. 
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 14 g/10 min

@Load 5.00 kg,
Temperature 200 °C
14 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 22.8 MPa
3310 psi
2.0 in/min; ASTM D638
Elongation at Break 35 %
35 %
2.0 in/min; ASTM D638
Modulus of Elasticity 2.07 GPa
300 ksi
2.0 in/min; ASTM D638
Flexural Strength 32.0 MPa
4640 psi
0.1 in/min; ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
0.1 in/min; ASTM D790
Izod Impact, Notched 1.23 J/cm
2.30 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
ASTM D648
Vicat Softening Point 94.0 °C
201 °F
ASTM D648
Flammability, UL94 V-0
V-0
0.059 in
Processing Properties Metric English Comments
Processing Temperature <= 249 °C
<= 480 °F
Rear Barrel Temperature 171 - 193 °C
340 - 379 °F
Middle Barrel Temperature 199 - 221 °C
390 - 430 °F
Front Barrel Temperature 210 - 243 °C
410 - 469 °F
Melt Temperature 210 - 243 °C
410 - 469 °F
Mold Temperature 32.0 - 54.0 °C
89.6 - 129 °F
Drying Temperature 68.0 °C
154 °F
Dry Time 2 hour
2 hour
Back Pressure 0.345 MPa
50.0 psi