Ineos Nova 6200 Super High Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Nova |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova 6200 Super High Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good toughness, Deep draw, Easy processing using all conventional methodsApplications: Thermoformed and molded packaging, Drink cups and lids, Structural foam, Custom sheetProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | Condition G |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 49 | 49 | ASTM D785 |
| Hardness, Rockwell M | 75 | 75 | |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 2.135 GPa | 309.7 ksi | ASTM D638 |
| Flexural Yield Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| Flexural Modulus | 1.965 GPa | 285.0 ksi | ASTM D790 |
| Izod Impact, Notched | 2.24 J/cm @Diameter 3.17 mm |
4.20 ft-lb/in @Diameter 0.125 in |
bar, 0.010" notch radius; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.51 @Frequency 1e+6 Hz |
2.51 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 15.7 kV/mm @Thickness 3.17 mm |
400 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | |
| Mold Temperature | 38.0 - 82.0 °C | 100 - 180 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R246AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kobe Steel KS15-3-3-3 Beta Titanium Alloy, AMS 4914, Solution treated and aged 482°C, 16 hrs - AC
- Spartech Royalite R52 PVC/Acrylic Fire Rated Sheet
- Lubrizol Estane® MVT 75AT3 Thermoplastic Polyurethane, Moisture Vapor Transmission
- ExxonMobil LL 6202.19 Injection Molding Resin
- DuPont Performance Polymers Delrin® FG500TL NC010 Acetal (POM) (Unverified Data**)
- Eurotec® Tecomid® NT40 MR40 NL HS PPA, 40% mineral reinforced, heat stabilized, natural
- 3M Scotch® 8959 Bi-Directional Filament Tape
- 3M Scotchcal™ ElectroCut™ 7125-130 Graphic Film
Copyright © lookpolymers.com All Rights Reserved