Ineos Nova 5511 High Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Nova |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova 5511 High Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good overall balance of properties, USP Class VIApplications: Audio cassettes and cartridges, Housewares, Toys, Industrial productsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | Condition G |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Yield Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| Flexural Modulus | 1.793 GPa | 260.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.98 J/cm @Diameter 3.17 mm |
3.71 ft-lb/in @Diameter 0.125 in |
bar, 0.010" notch radius; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.51 @Frequency 1e+6 Hz |
2.51 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 15.7 kV/mm @Thickness 3.17 mm |
400 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | |
| Mold Temperature | 38.0 - 82.0 °C | 100 - 180 °F |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6 PA6 WF30 Mineral Filled Nylon
- Garlock LEAK-GARDâ„¢ 3750 Compressed Aramid Fiber Gasketing
- Materion Beryllium Copper Alloy 25 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17200)
- Lubriplate SYN SYN-1601 PAO-Based Multi-Purpose Grease
- SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP (Asia Pacific)
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- Dow Corning 2-1865 Microemulsion
- Arlon 32400R040 0.040" (1.02 mm) Uncured Silicone Rubber on PET Carrier
- ChevronTexaco Crater® 5X
- Wacker Silicones Geniomer® 60 Silicone TPE
Copyright © lookpolymers.com All Rights Reserved