Ineos Nova 1510 High Heat Crystal Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Ineos Nova |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova 1510 High Heat Crystal Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow and high heat resistance, Excellent clarity, USP Class VIApplications: Injection moldingExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the physical and optical properties of the material.Properties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Condition G |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 | 75 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | ASTM D790 |
| Flexural Modulus | 3.037 GPa | 440.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.200 J/cm @Diameter 3.17 mm |
0.375 ft-lb/in @Diameter 0.125 in |
bar, 0.010" notch radius; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.59 @Wavelength 589.3 nm |
1.59 @Wavelength 589.3 nm |
sodium D line |
| Optical Density | 0.046 | 0.046 | 400-700 mm avg. |
| Transmission, Visible | 88 - 90 % | 88 - 90 % | at 550 mm |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.59 @Frequency 1e+6 Hz |
2.59 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 19.7 kV/mm @Thickness 3.17 mm |
500 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | |
| Mold Temperature | 38.0 - 82.0 °C | 100 - 180 °F |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® LA-0219-A LDPE Foam Resin
- LNP Thermocomp® LC-1006 Polyetheretherketone, Carbon Fiber Reinforcement (discontinued **)
- SABIC Innovative Plastics LNP LUBRILOY Lexan_WR6300 AES+PC+SAN
- Shin-Etsu Silicones KE-961U Silicone Elastomer
- Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- ExxonMobil HDPE HPA 020 Wire & Cable High Density Polyethylene Resin
- DuPont Teijin Films Mylar® EB11 Polyester Film, 300 Gauge
- CLAL-MSX SICLANIC S® TH4 Quenched Copper Alloy, 4/4 Hard, precipitation treated
- PolyOne Syncure™ S1042A Polyethylene, Crosslinked (XLPE)