SABIC Innovative Plastics Lexan® FXE1162T PC Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXE1162T PC Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* FXE1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. Lexan FXE1162T resin is available in GE Plastics' Visual fX* piano black, raven black and Illuminate color range only and may be an excellent candidate for a broad range of applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.090 % | 0.090 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.24 % @Temperature 23.0 °C |
0.24 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 19 g/10 min @Load 1.20 kg, Temperature 300 °C |
19 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 117.9 % | 117.9 % | Type I, 50 mm/min; ASTM D 638 |
| 119.4 % | 119.4 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.4 % | 5.4 % | 50 mm/min; ISO 527 |
| 5.7 % | 5.7 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.26 GPa | 328 ksi | 50 mm/min; ASTM D 638 |
| 2.34 GPa | 339 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.14 GPa | 310 ksi | 2 mm/min; ISO 178 |
| 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 6.18 J/cm @Temperature -30.0 °C |
11.6 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 7.36 J/cm @Temperature 23.0 °C |
13.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 74.0 J @Temperature 23.0 °C |
54.6 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
41.6 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 74.8 µm/m-°C @Temperature 23.0 - 80.0 °C |
41.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 76.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
42.4 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 76.4 µm/m-°C @Temperature 23.0 - 80.0 °C |
42.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate A/50; ASTM D 1525 |
| 138 °C | 280 °F | Rate B/50; ISO 306 | |
| 139 °C | 282 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- RheTech Products HP512-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- MMCC Cu/Al2O3 Particulate Copper Matrix Composite
- Teknor Apex Telcar® TL-1654G Thermoplastic Elastomer
- A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound
- ExxonMobil Mobil Pegasus 701 Series 40
- Polyram RamOfin PPH300G9 Polypropylene, 45% Glass Fiber
- EMS-Grivory Grivory® TSG-15/4 PA666-GF15