- Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (DAM), Injection Molding Grade
Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (DAM), Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (DAM), Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Triax® KU2-3154 is mineral reinforced, easy-flowing, injection molding grade, and comes in pellets. It has reduced moisture absorption and very low warpage.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Filler Content | 8 % | 8 % | ISO 3451-1 |
| Water Absorption | 1.3 % | 1.3 % | ISO 62 |
| Water Absorption at Saturation | 3.9 % | 3.9 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | Test Condition: 60x60x2; 260°C / MT 80°C; 500 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | Test Condition: 60x60x2; 260°C / MT 80°C; 500 bar; ISO 294-4 |
| Melt Flow | 8.5 g/10 min @Load 5.00 kg, Temperature 260 °C |
8.5 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 35 % | 35 % | 5 mm/min; ISO 527-1,-2 |
| 35 % | 35 % | 50 mm/min, Nominal; ISO 527-1,-2 | |
| Elongation at Yield | 2.9 % | 2.9 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 75.0 MPa | 10900 psi | 2 mm/min, @ 3.5% strain; ISO 178 |
| 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2; Parallel to Flow |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ISO 75-1,-2 |
| Vicat Softening Point | 105 °C @Load 5.10 kg |
221 °F @Load 11.2 lb |
50°C/hour; ISO 306 |
| 130 °C @Load 1.02 kg |
266 °F @Load 2.25 lb |
120°C/hour; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Shrinkage, MD | 0.10 % @Temperature 80.0 °C, Time 3600 sec |
0.10 % @Temperature 176 °F, Time 1.00 hour |
Post; Test Condition: 60x60x2; ISO 294-4 |
| Shrinkage, TD | 0.10 % @Temperature 80.0 °C, Time 3600 sec |
0.10 % @Temperature 176 °F, Time 1.00 hour |
Post; Test Condition: 60x60x2; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm @Thickness 1.00 mm |
1020 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.015 @Frequency 100 Hz |
0.015 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 294 |
| Injection Velocity | 40.0 mm/sec | 1.57 in/sec | Injection Molding; ISO 294 |
Users viewing this material also viewed the following:
- Inno-Comp INNOBATCH® PPH 3260 60% Chalk Filled Polypropylene Homopolymer
- Möller Medical NanoSkin 81 NanoCoating
- Superior Die Set FORTAL® HP Aluminum Alloy
- Aremco AREMCOLOX™ 502-1900-ZTA Dense Zirconia-Toughened Aluminum Oxide
- A. Schulman ComAlloy Comshield® 120 Copolymer Polypropylene, Electrically Conductive - Carbon Black Filled
- Huntsman Rexell® V8403 Cast Film Extrusion LLDPE (discontinued **)
- A. Schulman POLYTROPE™ TPP 530 Injection Molding Grade Olefinic Thermoplastic Elastomer
- HP Alloys Alloy 718, 50% Cold Worked, Aged
Copyright © lookpolymers.com All Rights Reserved