BASF Ultramid® N-265 NF3001 40% Mineral Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® N-265 NF3001 40% Mineral Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid N-265 NF3001 is a general purpose, 40% mineral reinforced PA6/6 that provides excellent flatness and dimensional stability in injection molding.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 5.1 %
5.1 %
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 100 MPa
14500 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
Tensile Modulus 9.90 GPa
1440 ksi
1mm/min; ISO 527
Flexural Modulus 9.30 GPa
1350 ksi
ISO Data
Izod Impact, Notched (ISO) 3.10 kJ/m²
1.48 ft-lb/in²
ISO Test
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179
2.50 J/cm²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
10 K/min
257 °C
495 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding