- Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Dry as Extruded
Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Dry as Extruded
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Dry as Extruded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 39.0 MPa | 5660 psi | ASTM D638 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ASTM D638 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | at 5% strain; ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 9.50 J/cm @Thickness 3.17 mm |
17.8 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 2.50 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
4.68 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 | |
| Impact Test | 61.0 J @Thickness 3.20 mm |
45.0 ft-lb @Thickness 0.126 in |
Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp, 3.3 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C @Thickness 3.17 mm |
163 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.50 mm |
140 °F @Thickness 0.0591 in |
UL746B |
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.50 mm |
140 °F @Thickness 0.0591 in |
UL746B |
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.50 mm |
140 °F @Thickness 0.0591 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
White color |
| HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
White color |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 9.70e+15 ohm-cm | 9.70e+15 ohm-cm | Tinfoil Electrodes; ASTM D257 |
| Surface Resistance | 8.30e+15 ohm | 8.30e+15 ohm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 16.7 kV/mm @Thickness 1.60 mm |
424 kV/in @Thickness 0.0630 in |
Short time under oil; ASTM D149 |
| Dissipation Factor | 0.024 @Frequency 1e+6 Hz |
0.024 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WY66L Polyvinyl Chloride, Flexible (PVC, Flexible)
- PTS Trimid® N66-G13LU 13% Glass Fiber Reinforced Utility Lubricated Nylon 6/6
- H.C. Starck Amperit® 703.053 Chromium Oxide (Cr2O3) 99.5%
- DuPont Elvaloy® 4924 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
- Zeon Chemicals Zetpol® 4310 Hydrogenated Nitrile Elastomomer
- Trelleborg Horda Cable E8413 Easy Strippable Semiconductive Shielding
- ExxonMobil Vacmul O 3 D
- Dow Corning 220 FLAKE RESIN
- Braskem LBH0120PBS LLDPE Blown Film Extrusion Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved