- Acrylonitrile Butadiene Styrene (ABS), Molded
- Styrolution NOVODUR® P3H-AT ABS, Injection Grade
Styrolution NOVODUR® P3H-AT ABS, Injection Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution NOVODUR® P3H-AT ABS, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding grade, antistatic, high gloss, improved chemical and dynamic resistance.Applications: Housings for telephones and household appliances.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | Saturation in water |
| Water Absorption at Saturation | 0.30 % | 0.30 % | |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 220 °C |
11 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | |
| Elongation at Yield | 2.6 % | 2.6 % | |
| Tensile Modulus | 2.50 GPa | 363 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| Vicat Softening Point | 96.0 °C | 205 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
|
| 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Lendell Nolatex® Latex Free Foam
- ITW Plexus Plexusâ„¢ MA920 Methacrylate Adhesive
- Henkel Hysol Benzoxazine 99110 Infusion Resin
- SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS
- A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene
- Ascend Performance Materials Vydyne® 47 BK11 Nylon 66, Impact Modified, Conditioned
- 3M Scotchkote™ FG 502 Epoxy Metal Repair
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N774 Filler
- LNP Lubricomp® OCL-4536 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant (discontinu
Copyright © lookpolymers.com All Rights Reserved