Ineos ABS TRIAXÂ® 1220 S ABS/Nylon Blend, Dry as Molded

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer	Ineos ABS
Trade Name	Triax®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS TRIAXÂ® 1220 S ABS/Nylon Blend, Dry as Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Extrusion and injection molding grade with good stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping behavior.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/inÂ³
Water Absorption	2.0 %	2.0 %	Saturation in water
Moisture Absorption at Equilibrium	2.0 %	2.0 %	Equilibrium at 50% RH
Water Absorption at Saturation	2.0 %	2.0 %
Linear Mold Shrinkage	0.0045 cm/cm	0.0045 in/in	ASTM D955
Melt Flow	3.0 g/10 min @Load 5.00 kg, Temperature 260 Â°C	3.0 g/10 min @Load 11.0 lb, Temperature 500 Â°F

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	93	93	ASTM D785
Tensile Strength, Ultimate	39.0 MPa	5660 psi	ASTM D638
Tensile Strength, Yield	39.0 MPa	5660 psi
Elongation at Break	150 %	150 %	ASTM D638
Elongation at Yield	3.6 %	3.6 %
Tensile Modulus	1.63 GPa	236 ksi
Flexural Yield Strength	70.0 MPa	10200 psi	at 5% strain; ASTM D790
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
Izod Impact, Notched	9.50 J/cm @Thickness 3.20 mm	17.8 ft-lb/in @Thickness 0.126 in	ASTM D256
	2.50 J/cm @Thickness 3.20 mm, Temperature -40.0 Â°C	4.68 ft-lb/in @Thickness 0.126 in, Temperature -40.0 Â°F	ASTM D256
Charpy Impact Unnotched	NB	NB
	2.20 J/cmÂ² @Temperature -30.0 Â°C	10.5 ft-lb/inÂ² @Temperature -22.0 Â°F
Charpy Impact, Notched	6.90 J/cmÂ²	32.8 ft-lb/inÂ²
Impact Test	49.0 J @Thickness 2.50 mm	36.1 ft-lb @Thickness 0.0984 in	Instrumented Total Impact; 2.5 mm thick, 12.5 mm dart, 40 mm clamp, 3.3 m/s; ASTM D3763

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	106 Âµm/m-Â°C @Temperature 20.0 Â°C	58.9 Âµin/in-Â°F @Temperature 68.0 Â°F
CTE, linear, Transverse to Flow	116 Âµm/m-Â°C @Temperature 20.0 Â°C	64.4 Âµin/in-Â°F @Temperature 68.0 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	91.0 Â°C	196 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	64.0 Â°C	147 Â°F
Vicat Softening Point	99.0 Â°C	210 Â°F
UL RTI, Electrical	60.0 Â°C	140 Â°F
UL RTI, Mechanical with Impact	60.0 Â°C	140 Â°F
UL RTI, Mechanical without Impact	60.0 Â°C	140 Â°F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Electrical Resistivity	9.70e+15 ohm-cm	9.70e+15 ohm-cm	ASTM D257
Surface Resistance	8.30e+15 ohm	8.30e+15 ohm	ASTM D257
Dielectric Constant	3.5 @Frequency 1e+6 Hz	3.5 @Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	17.0 kV/mm @Thickness 1.60 mm	432 kV/in @Thickness 0.0630 in	Short time under oil; ASTM D149
Dissipation Factor	0.024 @Frequency 1e+6 Hz	0.024 @Frequency 1e+6 Hz	ASTM D150