A. Schulman SCHULADUR® B GF15 15% Glass Fiber Reinforced PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULADUR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULADUR® B GF15 15% Glass Fiber Reinforced PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 3.175 mm |
0.0050 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 6.07 GPa | 880 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2205-22 CR-SX Fiberglass Reinforced SMC
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Black Peroxide Cure
- Braskem PB 601 LDPE Blow Molding Polyethylene (discontinued **)
- Materion BrushBronze® EQX20 Phosphorous Deoxidized Copper
- UBE UBESTA® 3030U Nylon 12 (After Zinc chloride aq. for 500 hours)
- Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Transverse Properties
- BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry)
- 3M Weatherban™ 606NF Acrylic Sealant
- A. Schulman POLYBATCH™ Grey LL80316/3 Concentrate Based In LLDPE
- SABIC Innovative Plastics Valox® VX5530 PBT (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved