Nilit Nilamid A3 H5 G6 30% Glass Reinforced PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid A3 H5 G6 30% Glass Reinforced PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid A3 H5 G6 has an outstanding mechanical performance and is 30% glass fiber reinforced. It is stabilized against chemical attack from peroxides and other oxidizing substances. It is used extensively for valve bodies and other parts that are in contact with water in household appliances.Key characteristics: Good overall mechanical performanceEase of processingGood surface finishGood thermal performance up to 140°CUL 94 RTI listing 130°C, 0.73 mmGood overall chemical resistance against most solvents and detergents, special stabilization against peroxide Information provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.70 % | 0.70 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 5.0 % | 5.0 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 170 MPa | 24700 psi | ISO 527, ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527, ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 250 MPa | 36300 psi | ISO 178, ASTM D790 |
| 160 MPa @Temperature 90.0 °C |
23200 psi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178, ASTM D790 |
| 5.50 GPa @Temperature 90.0 °C |
798 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179 |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 250 °C | 482 °F | 49 N; ISO 306, ASTM D1525 |
| 255 °C | 491 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Glow Wire Test | 650 °C @Thickness 3.20 mm |
1200 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 675 °C @Thickness 0.800 mm |
1250 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 | |
| 675 °C @Thickness 3.20 mm |
1250 °F @Thickness 0.126 in |
Glow Wire Ignition Temperature; IEC 695-2-13 | |
| 700 °C @Thickness 0.800 mm |
1290 °F @Thickness 0.0315 in |
Glow Wire Ignition Temperature; IEC 695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | 350 V @Thickness 3.20 mm |
350 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| 500 V @Thickness 3.20 mm |
500 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 280 - 295 °C | 536 - 563 °F | |
| Zone 1 | 270 - 290 °C | 518 - 554 °F | hopper |
| Zone 2 | 275 - 290 °C | 527 - 554 °F | |
| Zone 3 | 280 - 295 °C | 536 - 563 °F | |
| Zone 4 | 280 - 295 °C | 536 - 563 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | Do not melt above 300°C |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | Preferred |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | B22 | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 MPa |
Users viewing this material also viewed the following:
- Nye Lubricants 186B (SO) Synthetic Oil
- SABIC Innovative Plastics LNP FARADEX ES003E PEI
- Kolon SPESIN® KP513FLBL Multi Reinforced PBT Resin (discontinued **)
- DSM Akulon® K-FHGM24 (Cond.) 30% Glass/Mineral Reinforced, Nylon 6 (North America) (discontinued **)
- Industeel FORA 400 400 HB Wear Resistant Steel
- Sibur SKS-30 ARKPN 2nd Group Styrene-Butadiene Rubber (SBR)
- Silberline Sparkle Silvet® Premier 838-30-E1
- Wellman Wellamid® GF33AO99-HRBK 33% Glass Fiber Reinforced, Hydrolysis Resistant Nylon 66
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
Copyright © lookpolymers.com All Rights Reserved