Ineos ABS Lustran® Ultra 4105 ABS Pellets (Polycarbonate-modified), Medium High Heat Grade

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Ineos ABS
Trade Name Lustran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® Ultra 4105 ABS Pellets (Polycarbonate-modified), Medium High Heat Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® Ultra 4105 is medium high heat grade with superior impact resistance. It is PC-modified and has low emission. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Test Condition: 150x105x3; acc. ISO 2577
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Test Condition: 150x105x3; acc. ISO 2577
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 85.0 MPa
12300 psi
ISO 2039-1
Tensile Strength at Break 37.0 MPa
5370 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min; ISO 527-1,-2
Elongation at Break 15 %
15 %
50 mm/min, Nominal; ISO 527-1,-2
30 %
30 %
50 mm/min; acc. ISO 527-1,-2
Elongation at Yield 3.7 %
3.7 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.00 GPa
290 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 70.0 MPa
10200 psi
2 mm/min; ISO 178
Flexural Modulus 2.00 GPa
290 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 34.0 kJ/m²

@Temperature -30.0 °C
 16.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
42.0 kJ/m²

@Temperature 23.0 °C
 20.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Charpy Impact, Notched 3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
ISO 75-1,-2
Vicat Softening Point 106 °C

@Load 5.10 kg
 223 °F

@Load 11.2 lb
 50°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Flame Spread 34 mm/min

@Thickness 2.00 mm
 1.3 in/min

@Thickness 0.0787 in
 US-FMVSS; ISO 3795
Glow Wire Test 700 °C

@Thickness 2.00 mm
 1290 °F

@Thickness 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+16 ohm-cm
6.00e+16 ohm-cm
IEC 60093
Surface Resistance 2.00e+17 ohm
2.00e+17 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 60250
3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.0038

@Frequency 100 Hz
 0.0038

@Frequency 100 Hz
 IEC 60250
0.0086

@Frequency 1.00e+6 Hz
 0.0086

@Frequency 1.00e+6 Hz
 IEC 60250
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
Injection Molding; ISO 294