- Samsung Cheil Industries Infino® NE-1050 PC/ABS, Unreinforced FR
Samsung Cheil Industries Infino® NE-1050 PC/ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® NE-1050 PC/ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 59.8 MPa | 8680 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.26 GPa | 327 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.75 J/cm @Thickness 6.35 mm |
5.14 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 6.18 J/cm @Thickness 3.17 mm |
11.6 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C @Thickness 6.40 mm |
205 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | B/50; ISO R306 |
| 104 °C | 219 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 - 2.00 mm |
V-0 @Thickness 0.0591 - 0.0787 in |
Users viewing this material also viewed the following:
- Polikim Polypropylene
- SABIC Innovative Plastics LNP LUBRICOMP DFL34H PC
- FloMet Fe-3% Si Soft Magnetic Alloy
- Huntsman IROGRAN® A 92 P 4207 TPU-Polyether
- LATI Latiohm 90/13-09 PD01 G/10 PPOm, 10% Glass Fiber Reinforced
- Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion
- Barlog Plastics KEBAFORM C 901 TF POM Copolymer unreinforced, improved wear and friction
- 3M FM061 Indoor UL Recognized Brite Silver Polyester Label Products
- Formosa Plastics Formolene® LH5212 Injection Molding HDPE (discontinued **)
- Osprey Metals CE13 Al-Si Controlled Expansion Alloy
Copyright © lookpolymers.com All Rights Reserved