- Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled
Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer, Glass Filled, Impact Modified. Used in Automotive and Industrial applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | |
| Elongation at Break | 2.2 % | 2.2 % | |
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
| Flexural Yield Strength | 190 MPa | 27600 psi | |
| Flexural Modulus | 9.20 GPa | 1330 ksi | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | |
| Charpy Impact Unnotched | 4.60 J/cm² | 21.9 ft-lb/in² | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C | 31.7 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | ASTM D145 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | 30 - 60 sec @Thickness 1.50 mm |
30 - 60 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | NSF61 |
Users viewing this material also viewed the following:
- Garlock 9800 Compressed Carbon Fiber Gasketing, SBR Binder
- SABIC Innovative Plastics ULTEM 2310R PEI
- SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC
- A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT
- Diamond Polymers ABS 3501 Natural 1050
- DuPont Teijin Films Teijin® Tetoron® G2 Polyester Film, 75 Gauge
- Arkema Group Rilsan® MB 3945 Nylon 11, Rotomolding Grade (Dry)
- Asahi Kasei Thermylene® P-20TC-5100 Chemically Coupled Polypropylene Compound, 20% Talc Filled
Copyright © lookpolymers.com All Rights Reserved