- Idemitsu Kosan Xarec® N WA 5030 SPS, 30% Glass Filled
Idemitsu Kosan Xarec® N WA 5030 SPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® N WA 5030 SPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.19 % | 0.19 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 MPa | 23900 psi | |
| Elongation at Break | 2.4 % | 2.4 % | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | |
| Flexural Yield Strength | 235 MPa | 34100 psi | |
| Flexural Modulus | 9.40 GPa | 1360 ksi | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C | 23.9 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 7.40e+15 ohm-cm | 7.40e+15 ohm-cm | |
| Dielectric Constant | 3.3 | 3.3 | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | ASTM D145 |
| Dissipation Factor | 0.034 | 0.034 | IEC 60250 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness 1.50 mm |
7.0 - 15 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 1 - 3 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | Nylon/SPS blend | |
| Optimized dimensional stability |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V95X Fluoroelastomer Compound
- Network Polymers Softflex® 0470
- PSM Industries Pacific Sintered Metals Nickel Silver BZN-131-U Powdered Metal
- SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer
- Polyram Polytron P40N11 Polypropylene, 40% Long Glass Fibers
- Cytec (Conap) FR-1210 / EA-117 Conapoxy® Resin / Conacure® Hardener
- Crucible Steel 304L Chromium-Nickel Steel
- 3M 9675 Adhesive Transfer Tapes with Adhesive 350
- LG Chemical LUPOY SC1004ML PC, High Impact
Copyright © lookpolymers.com All Rights Reserved