Nilit FRIANYL B63 W-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 W-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.6 % | 1.5 - 2.6 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0060 - 0.013 cm/cm | 0.0060 - 0.013 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 174 MPa | 25200 psi | ISO 2039-1 |
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 4.50 J/cm² @Temperature -40.0 °C |
21.4 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| 1.50 J/cm² | 7.14 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 575 V | 575 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2875 TPE, PP Overmold or Standalone use
- Overview of materials for EMAAA Terpolymer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plastolein 9057 Plasticizer
- Honeywell Aegis™ HFX High Barrier Nylon (discontinued **)
- Mateck MgAl2O4
- Lucas-Milhaupt BRAZE 750 (Hard) Silver Based Cadmium Free Filler Metal
- Eurostar Staramide AK6 PA66, 30% Mineral Reinforced, Injection Molding
- Arlon 30570R020 0.020" (0.508 mm) Uncured/Unsupported Silicone Rubber on a Release Carrier
- Solvay Specialty Polymers Algoflon® E2 BP PTFE (Polytetrafluoroethylene) (discontinued **)
- DuPont Elvax® 3176CW-3 Ethylene Vinyl Acetate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved