Idemitsu Kosan Xarec® EA 533 SPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® EA 533 SPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass Filled, Ignition Resistant, Impact Modified. Used in electronic and electrical applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 10.7 GPa | 1550 ksi | |
| Flexural Yield Strength | 195 MPa | 28300 psi | |
| Flexural Modulus | 10.5 GPa | 1520 ksi | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | |
| Charpy Impact Unnotched | 4.20 J/cm² | 20.0 ft-lb/in² | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C | 21.7 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| UL RTI, Electrical | 125 °C | 257 °F | UL746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL746B |
| UL RTI, Mechanical without Impact | 120 °C | 248 °F | UL746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | ASTM D145 |
| Dissipation Factor | 0.0020 | 0.0020 | IEC 60250 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 1.50 mm |
60 - 120 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPX8R PC Copolymer
- Freudenberg Simrit N466 Nitrile Elastomer (NBR)
- Stir SpA SG 78 K8 (PVC)
- A. Schulman FORMION™ FI 389 Ionomer
- A. Schulman POLYBATCH™ Bright While LL80250 Concentrate Based In LLDPE
- EMS-Grivory Grivory® AZ 3/2 PA66
- CMW® D54F Pre-oxidized Silver Cadmium Oxide Contact Material ASTM B781, Table 3
- Bapolene® 4052F Polypropylene, Blown Film Grade
- Aptek 2120 PMF Low modulus urethane staking compound
- Quadrant EPP Quadrant PSU unfilled, extruded (ISO Data)
Copyright © lookpolymers.com All Rights Reserved