- Huntsman IROGRAN® A 98 E 4066 Polyester-Based TPU-High Performance Grade
Huntsman IROGRAN® A 98 E 4066 Polyester-Based TPU-High Performance Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 98 E 4066 Polyester-Based TPU-High Performance Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 98 E 4066 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are very short cycle times and high dimensional stability. Performance Features: Short cycle times High demolding stability High production rates High wear resistance High hydrolysis resistance Applications: For the production of technical parts, wheels and rollers, coupling halfs, sprocket wheels, buffers.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D995 |
| Melt Index of Compound | 15 g/10 min @Load 21.6 kg, Temperature 210 °C |
15 g/10 min @Load 47.6 lb, Temperature 410 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | ASTM D2240 |
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | DIN 53504 |
| Elongation at Break | 530 % | 530 % | DIN 53504 |
| 100% Modulus | 0.0140 GPa | 2.03 ksi | DIN 53504 |
| 300% Modulus | 0.0250 GPa | 3.63 ksi | DIN 53504 |
| Rebound | 30 % | 30 % | Bayshore; ASTM D2632 |
| Tear Strength | 135 kN/m | 770 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 30 % @Temperature 23.0 °C, Time 252000 sec |
30 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 45 % @Temperature 70.0 °C, Time 86400 sec |
45 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection Molding | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection Molding |
| 185 - 200 °C | 365 - 392 °F | ||
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection Molding |
Users viewing this material also viewed the following:
- Nylene® 401, Nylon 6, at 50% Relative Humidity
- Polystrand ThermoPro™ IS7015 Unitape Unidirectional Polypropylene-Glass Composite
- Pyrotek Wollite 50 Insulating Castable
- Quadrant EPP Acetron® LSG POM-C, LSG grade, extruded (ISO Data)
- Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) (Unverified Data**)
- Braskem Flexus® 9210 LLDPE Blown Film Extrusion (discontinued **)
- Teknor Apex APEX® 3610-80 Polyvinyl Chloride, Flexible
- Denka LCS Z1070 Thermoplastic Elastomer, Extrusion grade (general)
- BASF Ultramid® B3UG4 BK 23215 20% Glass Filled PA66 FR (Conditioned)
- Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Dry)
Copyright © lookpolymers.com All Rights Reserved