Gromax BFG30-AH00B2 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-AH00B2 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 275 °C |
60 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 91 | 91 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 157 MPa | 22800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.5 % | 3.5 % | 50 mm/min; ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.24 GPa | 1190 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 6.03 J/cm² @Temperature 23.0 °C |
28.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.02 J/cm² @Temperature 23.0 °C |
4.85 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- LNP Lubricomp® OFL-4036 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant (discontinued **)
- Isoflon Tisoflon® 5K Polytetrafluoroethylene Coated Kevlar Fabric
- Silberline Aquasil® "BP" 205
- Plastics Group Polifil® GFPPCC-40 40% Glass Reinforced Polypropylene
- Unipetrol Middle Oil Hydrogenate
- A. Schulman POLYBATCH™ U-7000-HS Blowing Agent Concentrate Based In HIPS
- Goodfellow TPX® DX310 Coating/Extrusion Grade Polymethylpentene
- China Tungsten YG3 Tungsten Carbide for Cutting Tools
- DuPont Performance Polymers VESPEL TP-8311 Polyimide
- Aclo Accutech Polypropylene Homopolymer HP0336C20L1 Calcium Reinforced
Copyright © lookpolymers.com All Rights Reserved