Gichem GIBLEND E45X3/VO ABS - Polycarbonate - PC/ABS Flame Retardant (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gichem GIBLEND E45X3/VO ABS - Polycarbonate - PC/ABS Flame Retardant
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Blend PC-ABS self-extinguishing class V0 medium fluidity. Medium injection speed.Information provided by GICHEM Gruppo Industriale Chimico
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 3.50 J/cm | 6.56 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525/A |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 100 °C | 212 °F | 2 hours |
Users viewing this material also viewed the following:
- Ovation Polymers OpteSTAT™ MB SF 6000 Polyether Sulfone based Carbon Nanotube Compound
- Kostat BK-STAT
- SABIC Innovative Plastics LNP THERMOCOMP JF006 PES
- Topas Advanced Polymers TOPAS® 5013F-04 Cyclic Olefin Copolymer (COC)
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- Eastman Aspira EN177 Copolyester Resin for Extrusion Blow Molding
- Ecomass® 1080BI64 Filled Polyamide
- CRP Technology 8601 Aerospace Grade Power Metallurgy Aluminum Alloy
- 3M 9416 Repositionable Tape
- 3M FV098 Soft Translucent Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved