Fiberfil® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.011 - 0.014 cm/cm @Thickness 3.17 mm |
0.011 - 0.014 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.013 - 0.016 cm/cm @Thickness 6.35 mm |
0.013 - 0.016 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ASTM D638 |
| Flexural Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 2.08 J/cm @Thickness 3.17 mm |
3.90 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- MV Labs CD100 Cd(C2H3O2)2·xH2O Cadmium acetate hydrate
- Polymax® Maxelast® F02-137B TPE, Halogen Free Extrusion Grade
- Huntsman Araldite GT 7226 Bisphenol A Epoxy Solid Resin
- Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled
- Teknor Apex Uniprene® UN-2598D Thermoplastic Vulcanizate
- Westlake Hifor SC74557 Linear Low Density Polyethylene
- Lubrizol ESTANE® 58881 Ether Based Thermoplastic Polyurethane
- EMS-Grivory Grivory® L 25 NZ ESD PA12
- Chosun Refractories CSN-309N Plate Brick
- ATI Allegheny Ludlum Type 332 Stainless Steel, UNS N08800
Copyright © lookpolymers.com All Rights Reserved