NOVA Chemicals Sclair® 19A Homopolymer HDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 19A Homopolymer HDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.0300 cc-mm/m²-24hr-atm | 0.0762 cc-mil/100 in²-24hr-atm | 38 µm film; ASTM D1434 |
| Water Vapor Transmission | 0.800 g/m²/day | 0.0515 g/100 in²/day | 38 µm film;; ASTM D1434 |
| 3.41 g/m²/day | 0.220 g/100 in²/day | ||
| Oxygen Transmission | 41.0 cc-mm/m²-24hr-atm | 104 cc-mil/100 in²-24hr-atm | or 1070 cc/m²-atm-24 hr per 38 µm film; 38°C; 90% RH Difference |
| Oxygen Transmission Rate | 1705 cc/m²/day | 109.8 cc/100 in²/day | |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.72 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 27.0 MPa | 3920 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Secant Modulus, MD | 0.830 GPa | 120 ksi | ASTM D882 |
| Secant Modulus, TD | 1.33 GPa | 193 ksi | ASTM D882 |
| Coefficient of Friction | 0.30 | 0.30 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 0.550 g/micron | 14.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 12.42 g/micron | 315.5 g/mil | ASTM D1922 |
| Dart Drop | 0.890 g/micron | 22.6 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 39.0 MPa | 5660 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 78 % | 78 % | ASTM D1003 |
| Gloss | 5.0 % | 5.0 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- MV Labs CA200 CaBr2·xH2O Calcium bromide hydrate
- Polikim EFALON® B-40 PTFE, 40% Bronze Filled
- PolyOne Bergamid™ A70 UF natur V0 Polyamide 66 (Nylon 66)
- Arlon A1030-R008-12 0.030" (0.762 mm) Fully Cured Fusible Silicone Rubber - Extruded Fusible Tape (disco
- Teknor Apex Flexalloy® 9100-75 Polyvinyl Chloride Elastomer
- Tra-Con Tra-Bond 224-1 Rapid Room Temperature Cure Epoxy Adhesive
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Hercoflex 600 Plasticizer
- 3M 225 Silver Weather-Resistant Masking Tape
- LATI LATISHIELD 90/13-07A-V1 Modified Polyphenylene Oxide (PPOm) Base E.M.I. Shielding Plastic (UL94 V-1) (di
Copyright © lookpolymers.com All Rights Reserved