- Fiberfil® PP-61/CC/20 Polypropylene Copolymer, 20% Calcium Carbonate
Fiberfil® PP-61/CC/20 Polypropylene Copolymer, 20% Calcium Carbonate
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-61/CC/20 Polypropylene Copolymer, 20% Calcium Carbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm @Thickness 3.17 mm |
0.012 - 0.014 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.014 - 0.016 cm/cm @Thickness 6.35 mm |
0.014 - 0.016 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 75 - 85 | 75 - 85 | ASTM D785 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 1.65 GPa | 240 ksi | ASTM D638 |
| Flexural Strength | 29.0 MPa | 4200 psi | ASTM D790 |
| Flexural Modulus | 1.52 GPa | 220 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 215 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics Valox® V9500GW PET+PC (Europe-Africa-Middle East)
- Teknor Apex APEX® 590 Polyvinyl Chloride, Flexible
- Samsung Cheil Industries Starex® SF-101H Expandable Polystyrene (EPS) FR
- A. Schulman POLYBATCH™ FTA-50-P Concentrate Based In LLDPE
- Borealis Borstar® MB7542 High Density Polyethylene for Injection Molding
- Addiplast Addinyl B2 R Nylon 6
- BASF Ultradur® B 4300 G6 HR 30% Glass Filled PBT
- Chevron Phillips Dynex™ D605C3 Enhanced LLDPE Blown Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved