Eurotec® Tecoform® PO20 NL IL POM, impact modified, natural
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified |
| Manufacturer | Eurotec |
| Trade Name | Tecoform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecoform® PO20 NL IL POM, impact modified, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Tensile Modulus | 1.10 GPa | 160 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | |
| Feed Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | Throat |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | |
| Hold Pressure | 80.0 - 100 MPa | 11600 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- LyondellBasell PE Propylene glycol ethyl ether
- Heatbath/Park Polyquench 20 Water-Based Quenchant
- China Tungsten YG6C Tungsten Carbide
- Eurotec® Tecolen® CP10 GR50 NL PPCP, 50% glass fiber reinforced, natural
- Abatron AboCast 8103-24 High-Performance Dielectric Epoxy
- 3M 256 Colored Paper Tape
- 3M AC-251 Black Class B-1 Aerospace Sealant
- Aclo Accutech Polypropylene Homopolymer HP0336G30CL Glass Reinforced Coupled
- Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved